铝合金的物理特性1

　　合金溶点范围密度热膨胀系数比热容量弹性耐力状态热导电性能电阻率

　　℃kg.m-3(10-6K-1)(20/100℃)J/(kg.K)(0/100℃)MpaW/(m.K)20℃10-3ūΩm20℃

　　1100645/657271023.690469000全部22529.2

　　1050A645/658270023.589969000O22929.2

　　2024502/638277021.187573000O/T3/T4/T6193/121/15134/56/45

　　5005632/652270023.790069000全部20133

　　5657638/657269023.790069000全部20532

　　5049620/650271023.7

　　5251597/650268023.8900全部13944

　　5052605/650268023.890070000全部13850

　　5454602/646266023.790070000全部13450

　　5754590/645267023.890070000全部13253

　　5086585/640266023.890071000全部12656

　　5182577/638265024.190469500O12356

　　5083574/638266024.290071000O11759

　　5019568/638264024.1904O11759

　　铝合金的物理特性2

　　合金溶点范围密度热膨胀系数比热容量弹性耐力状态热导电性能电阻率

　　℃kg.m-3(10-6K-1)(20/100℃)J/(kg.K)(0/100℃)MpaW/(m.K)20℃10-3ūΩm20℃

　　5356574/630264024.2904O11759

　　6060615/655270023.494569500T520033

　　6101621/654269023.589569000T621830

　　6005A607/654270023.694069500T1/T5180/18837/36

　　6106610/655270023.569500T518035

　　6063615/655269023.490069500O/T6/T8218/20129/32

　　6082570/645271023.596069500T617442

　　6061582/652270023.689669500O/T4/T6180/153/16737/43/40

　　6262582/652271023.469500T617238

　　7020604/645278023.187571500O/T6/T8166/13740/49

　　7075477/635280023.496072000T6/T73130/13552/43

　　7050490/635283023.586071500O/T76180/15436/43

　　7049A477/627282023.496072000T615443

　　7072640/655271023.589068000O22728